FibArm Resin 530+
Intended for impregnation of the external reinforcement system, two component epoxy resin with an improved composition, due to which its key characteristics and physical properties were improved
FibArm Resin 530+ is recommended for use with fabrics and carbon fiber tapes, the density of which exceeds 300 g / m2, used for external reinforcement of structures using FibArm technology.
The technology of external reinforcement using carbon tapes will allow to solve a whole range of problems associated with the loss of the structural bearing capacity, thereby not only restoring existing deficiencies, but also increasing the bearing capacity in the shortest possible time and with significantly lower labor costs in comparison with traditional reinforcement methods.
The system will increase periods between renovations, as well as significantly increase the life-time of all structural elements.
FibArm Resin 530+ is recommended for use with fabrics and carbon fiber tapes, the density of which exceeds 300 g / m2, used for external reinforcement of structures using FibArm technology.
The technology of external reinforcement using carbon tapes will allow to solve a whole range of problems associated with the loss of the structural bearing capacity, thereby not only restoring existing deficiencies, but also increasing the bearing capacity in the shortest possible time and with significantly lower labor costs in comparison with traditional reinforcement methods.
The system will increase periods between renovations, as well as significantly increase the life-time of all structural elements.
Main features:
Improved adhesion to many different surfaces, applicable on concrete, stone, wood, metal, and carbon fiber
High viability
Once dry, the epoxy is completely eco-friendly
Thick enough, which makes it more convenient to carry out strengthening using low-density tape.
Simplification of the process and speed of impregnation of carbon fabric
Reduction of epoxy consumption by 15-20%
The epoxy compound has passed all the required certification and has the following documents:
Packaging:
Two metal buckets, component A - 15 kg and B - 7.5 kg
The minimum order quantity is 1 set, 22.5 kg.
Warranty period of storage
Guaranteed shelf life is 24 months from the date of manufacture. It is necessary to store and transport the material in holistic factory packaging, at a temperature of + 5 ° C to + 30 ° C. When transporting and storing material, it is prohibited to install pallets on top of one another.
- Certificate of conformity with the requirements of TC (technical conditions, Russia)
- Certificate of conformity of technical fire safety regulations
- Sanitary and epidemiological conclusion on compliance with the requirements of odor metric and sanitary-chemical indicators.
Packaging:
Two metal buckets, component A - 15 kg and B - 7.5 kg
The minimum order quantity is 1 set, 22.5 kg.
Warranty period of storage
Guaranteed shelf life is 24 months from the date of manufacture. It is necessary to store and transport the material in holistic factory packaging, at a temperature of + 5 ° C to + 30 ° C. When transporting and storing material, it is prohibited to install pallets on top of one another.
Physical properties
Compound color
Density of CompoundA + B (at t20 ± 2 ° C)
Viability (at t20 ± 2 ° C)
Adhesion (bond strength)
Shear strength of adhesive samples
Mixing ratio (A: B)
Compound color
Density of CompoundA + B (at t20 ± 2 ° C)
Viability (at t20 ± 2 ° C)
Adhesion (bond strength)
Shear strength of adhesive samples
Mixing ratio (A: B)
Homogeneous thixotropic composition
Comp. A - colorless
Comp. B - light yellow
<1.18 g/cm3
> 60 min
> 2.5 MPa
>10 MPa
3:1 (weight ratio)
Comp. A - colorless
Comp. B - light yellow
<1.18 g/cm3
> 60 min
> 2.5 MPa
>10 MPa
3:1 (weight ratio)